锂尾矿砂制备蒸压加气混凝土砌块的实验研究
作者:权宗刚,陈媛媛,马茸茸,刘蓉
(西安墙体材料研究设计院有限公司,陕西 西安 710061)
摘要:以锂尾矿砂为主要硅质原料制备蒸压加气混凝土砌块,研究了球磨时间、配方、静停养护时间及静停温度等对蒸压加气混凝土砌块干密度、抗压强度等性能的影响。研究表明,最优配方为:锂尾矿砂65%、生石灰13%、水泥17%、石膏5%、铝粉0.06%,水固比为0.55;最优球磨时间25 min,静停养护时间3 h,静停温度60 ℃,制得的砌块抗压强度可达到3.62 MPa,干密度为597 kg/m3。
关键词:锂尾矿砂;蒸压加气混凝土;配方;抗压强度;干密度
中图分类号:TU528.2 文献标识码:A 文章编号:1001-702X(2022)02-0120-04
Experimental study on preparation of autoclaved aerated concrete block from lithium tailings
QUAN Zonggang,CHEN Yuanyuan,MA Rongrong,LIU Rong
(Xi'an Walling Material Research and Design Institute Co. Ltd.,Xi'an 710061,China)
Abstract:Autoclaved aerated concrete blocks were prepared with lithium tailings as the main siliceous raw material in this study. The effects of ball-milling time,formula,static stop time and static stop temperature on the dry density and compressive strength of autoclaved aerated concrete blocks were studied. The results show that the optimum formula is:lithium tailings 65%,quicklime 13%,cement 17%,gypsum 5%,aluminum powder 0.06%,water-solid ratio 0.55;The optimum milling time is 25 min,the static stop curing time is 3 h. The static stop temperature is 60 ℃. The compressive strength of the obtained block is 3.62 MPa and the dry density is 597 kg/m3.
Key words:lithium tailings,autoclaved aerated concrete,formula,compressive strength,dry density