轻质膏状腻子的制备与性能研究
作者：郭锋
（江苏尼高科技有限公司，江苏 常州 213141）
摘要：以气凝胶、空心微珠为主要超轻骨料制备的轻质膏状腻子，通过对导热系数、附加热阻、粘结强度等性能的测试，探究了超轻骨料、乳液等对轻质膏状腻子性能的影响。结果表明，以气凝胶颗粒A和空心微珠为主要超轻骨料制备的轻质膏状腻子具有良好的保温隔热功能，其导热系数仅为0.035 W/（m·K），5 mm厚轻质膏状腻子涂层的附加热阻可达0.346 m2·K/W。
关键词：气凝胶；空心微珠；轻质膏状腻子；附加热阻
中图分类号：TU55+.1.3 文献标识码：A 文章编号：1001-702X（2022）10-0078-03
Study on preparation and properties of lightweight colloidal putty
GUO Feng
（Jiansu Nigao Science and Technology Co. Ltd.，Changzhou 213141，China）
Abstract：In this paper，a lightweight colloidal putty was prepared with aerogels and hollow glass sphere as main ultra-light aggregate. Through the measurement of thermal conductivity，adding thermal resistance，bonding strength and other performance indicators，the effects of ultra-light aggregate and emulsion on the performance of lightweight colloidal putty were explored. The results show that the lightweight paste putty made of aerogel particles A and hollow microbeads has good thermal insulation function，its thermal conductivity is 0.035 W/（m·K），and the additional thermal resistance of the 5 mm thick paste putty coating is 0.346 m2·K/W.
Key words：aerogels，hollow glass sphere，lightweight colloidal putty，additional thermal resistance